Formation of Dense Pore Structure by Te Addition in Bi0.5Sb1.5Te3: An Approach to Minimize Lattice Thermal Conductivity
Year: 2013
Type: article
Abstract: We herein report the electronic and thermal transport properties of p‐type Bi0.5Sb1.5Te3 polycrystalline bulks with dense pore structure. Dense pore structure was fabricated by vaporization of residual Te during the pressureless annealing of spark plasma sintered bulks of Te coated Bi0.5Sb1.5Te3 powders. The lattice thermal conductivity was effectively reduced to the value of 0.35 W m−1 K−1 at 300 K mainly due to the phonon scattering by pores, while the power factor was not significantly affected. An enhanced ZT of 1.24 at 300 K was obtained in spark plasma sintered and annealed bulks of 3 wt.% Te coated Bi0.5Sb1.5Te3 by these synergetic effects.
Source: Journal of Nanomaterials
DOI: 10.1155/2013/905389
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $2,375
Awards: G3384177124, G6273532949
OpenAlex ID: W1976486226