Low‐intensity pulsed ultrasound increases cellular uptake of superparamagnetic iron oxide nanomaterial: Results from human osteosarcoma cell line U2OS
Year: 2010
Type: article
Abstract: PURPOSE: To determine whether low-intensity pulsed ultrasound (LIPUS) is able to facilitate the uptake of a superparamagnetic iron oxide (SPIO) nanomaterial by cells that do not express high endocytosis capacity. MATERIALS AND METHODS: The human osteosarcoma cell line U2OS and a silica-coated SPIO functionalized peripherally with amines groups (overall diameter 8 nm) were used in this study. Adherent U2OS cells were labeled with SPIO by incubating with culture media containing the SPIO at 4.5 microg[Fe]/mL. LIPUS with the same parameters as those used in clinical application to accelerate bone fracture healing (1.5 MHz, duty cycle 1:4, spatial-average temporal-average intensity 30 mW/cm(2)) was applied to the cells at the beginning of the labeling process for 0, 0.5, 1, or 3 hours. The total incubation time with SPIO was 12 hours. SPIO labeling efficiency was evaluated with Prussian blue staining and a blueness measurement method, and magnetic resonance imaging (MRI) of cell pellets via measuring areas of SPIO-induced signal void. RESULTS: Both Prussian blue staining and in vitro MRI demonstrated that LIPUS application increased the SPIO nanomaterial labeling efficiency for U2OS cells in an exposure-duration-dependent manner. CONCLUSION: This study is a "proof of concept" that LIPUS can facilitate the cellular take-up of SPIO nanomaterial.
DOI: 10.1002/jmri.22173
Language: English
Subfield: Biomedical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: bronze
OpenAlex ID: W2004620328