Effect of Calcium and Magnesium Addition on the Cast Microstructure Grain Size of HSLA Steel
Year: 2014
Type: article
Abstract: A kind of HSLA steel is designed in this experiment. The thermal stability second phase particles which would not be dissolved or aggregated at high temperature will be expected by means of adding calcium and magnesium into the steel in the form of Si-Ca alloy and Mg-Zr alloy, respectively. The effect of calcium and magnesium addition on the cast microstructure grain size of HSLA steel was analysed. The grain size of the cast microstructure in each sample was measured by the metalloscope observation method. The results show that a large amount of oxides generated from the adding Ca and Mg elements into the steel can accelerate the nucleation and refrain the grain growth, so the grains are refined. In the process of improving temperature, the oxides of Ca and Mg elements located in the interior of austenite can accelerate the nucleation and impede the grain growth. Almost every grain becomes finer after adding Ca and Mg elements. When adding 5wt% Mg, the mean grain size is the smallest, 0.712 mm, while the biggest grain size is 1.115mm in raw steel. The grain size in Mg 5wt% steel is refined by 36.1% in contrast with the raw steel. According to the adding amounts of Ca and Mg elements in experimental steel, the range of the mean grain size is from 0.712 mm to 0.975 mm.
Source: Applied Mechanics and Materials
Authors: Yan Liu, Kai Wang, Yang Liu, Jian Ming Wang
Institution: Shenyang University
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
OpenAlex ID: W2091602892