Year: 1995
Type: article
Abstract: The sintered PbTe compacts were prepared by HIP 2hour at 800°C under 22.5MPa in Ar atmosphere. The relative density of sample were 92-94%.The grain sizes of HIPed specimen were a little smaller than those of normal sintered specimen. The Seebeck coefficient of HIPed specimen were a value of 440μV/K at 220°C. The specimens behave n-type semiconductor at more than 320°C, although this specimen is p-type semiconductor. This behavior seems to be due to the oxidation of dopant. The electrical resistivities of HIPed specimen were larger than those of normal sintered specimen. The thermal conductivity of HIPed specimen was a value of 2.657 W/mK at 70°C. Figure of merit for HIPed specimen was calculated smaller than that of normal sintered specimen. KEY WORDSPbTe, sintering, HIP, microstructure.
DOI: 10.2497/jjspm.42.507
Authors: Mitsuhiro Iizuka, Sunao Sugihara
Institution: Shonan Institute of Technology
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W2318576498