Flexural Strength of Alumina Ceramics: Weibull Analysis

Year: 2010

Type: article

Abstract: In this paper, flexural strength,  fs , of cold isostatically pressed (CIP) high purity alumina ceramics was determined by the three-point bend test.It was found that flexural strength shows a large variation and can be described by a two-parameter Weibull distribution function, with the scale parameter  0 , and the Weibull modulus m.These parameters were determined by the linear regression using the measured values of  fs .It was found that the measured flexural strength,  fs , of alumina ceramics follows the Weibull distribution.The flexural strength values were found to range from 266.7 to 357.5 MPa.

Source: Repository of Faculty of Mechanical Engineering and Naval Architecture University of Zagreb

Authors: Lidija Ćurković, Ante Bakić, Janoš Kodvanj, Tatjana Haramina

Language: English

Topic: Advanced ceramic materials synthesis

Subfield: Ceramics and Composites

Field: Materials Science

Domain: Physical Sciences

Open Access status: green

OpenAlex ID: W2474384415

FWCI: 0.343

Cites: 11

Cited by: 50

Related to: 10