Utilizing Co2+/Co3+ Redox Couple in P2‐Layered Na0.66Co0.22Mn0.44Ti0.34O2 Cathode for Sodium‐Ion Batteries

Year: 2017

Type: article

Abstract: Developing sodium‐ion batteries for large‐scale energy storage applications is facing big challenges of the lack of high‐performance cathode materials. Here, a series of new cathode materials Na0.66CoxMn0.66–xTi0.34O2 for sodium‐ion batteries are designed and synthesized aiming to reduce transition metal‐ion ordering, charge ordering, as well as Na+ and vacancy ordering. An interesting structure change of Na0.66CoxMn0.66–xTi0.34O2 from orthorhombic to hexagonal is revealed when Co content increases from x = 0 to 0.33. In particular, Na0.66Co0.22Mn0.44Ti0.34O2 with a P2‐type layered structure delivers a reversible capacity of 120 mAh g−1 at 0.1 C. When the current density increases to 10 C, a reversible capacity of 63.2 mAh g−1 can still be obtained, indicating a promising rate capability. The low valence Co2+ substitution results in the formation of average Mn3.7+ valence state in Na0.66Co0.22Mn0.44Ti0.34O2, effectively suppressing the Mn3+‐induced Jahn–Teller distortion, and in turn stabilizing the layered structure. X‐ray absorption spectroscopy results suggest that the charge compensation of Na0.66Co0.22Mn0.44Ti0.34O2 during charge/discharge is contributed by Co2.2+/Co3+ and Mn3.3+/Mn4+ redox couples. This is the first time that the highly reversible Co2+/Co3+ redox couple is observed in P2‐layered cathodes for sodium‐ion batteries. This finding may open new approaches to design advanced intercalation‐type cathode materials.

Source: Advanced Science

DOI: 10.1002/advs.201700219