Abstract: Thin films of PbSe of 400–600 nm in thickness, were obtained via chemical deposition from a solution containing lead nitrate, thiourea and selenosufate. SnSe thin films of 90–180 nm in thickness, were also obtained by chemical deposition from a solution containing selenosulfate. Optical and electrical properties of these thin films were significantly altered by heating them in selenium vapor at 300 °C. Thin film PbSe has a bandgap (E g ) of 1.17 eV (direct gap, forbidden transitions), which decreases to 0.77 eV when it has been heated. Its electrical conductivity ( σ ) is p-type: 0.18 Ω −1 cm −1 (as-prepared), and 6.4 Ω −1 cm −1 when heated. Thin film SnSe is of orthorhombic crystalline structure which remains stable when heated at 300 °C, but its E g increases from 1.12 eV (indirect) in as-prepared film to 1.5 eV (direct, forbidden transitions) upon heating. Its electrical conductivity is p-type, which increases from 0.3 Ω −1 cm −1 (as-prepared) to 1 Ω −1 cm −1 when heated (without Se-vapor). When SnSe film is heated at 300 °C in the presence of Se-vapor, they transform to SnSe 2 , with E g of 1.5 eV (direct, forbidden) with n-type electrical conductivity, 11 Ω −1 cm −1 . The Seebeck coefficient for the PbSe films is: +0.55 mV K −1 (as prepared) and +0.275 mV K −1 (heated); for SnSe films it is: +0.3 mV K −1 (as prepared) and +0.20 mV K −1 (heated); and for SnSe 2 film, − 0.35 mV K −1 . A five-element PbSe-SnSe 2 -PbSe-SnSe 2 -PbSe thermoelectric device demonstrated 50 mV for a temperature difference ΔT = 20 °C (2.5 mV K −1 ). For SnSe-SnSe 2 -SnSe-SnSe 2 -SnSe device, the value is 15 mV for ΔT = 20 °C (0.75 mV K −1 ). Prospect of these thin films in thermoelectric devices of hybrid materials, in which the coatings may be applied on distinct substrate and geometries is attractive.
Institution: Universidad Nacional Autónoma de México
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: bronze
Awards: G1004501039, G874818967
OpenAlex ID: W2782530928