Effect of Oxygen Nonstoichiometry on Electrical Conductivity and Thermopower of Gd0.2Sr0.8FeO3−δ Ferrite Samples

Year: 2018

Type: article

Abstract: The behavior of the resistivity and thermopower of the Gd0.2Sr0.8FeO3−δ ferrite samples with a perovskite structure and the sample stability in an inert gas atmosphere in the temperature range of 300–800 K have been examined. It has been established that, in the investigated temperature range, the thermoelectric properties in the heating‒cooling mode are stabilized at δ ≥ 0.21. It is shown that the temperature dependencies of the resistivity obtained at different δ values obey the activation law up to the temperatures corresponding to the intense oxygen removal from a sample. The semiconductor‒semiconductor electronic transitions accompanied by a decrease in the activation energy have been observed with increasing temperature. It is demonstrated that the maximum thermoelectric power factor of 0.1 µW/(cm·K2) corresponds to a temperature of T = 800 K.

Source: Materials

DOI: 10.3390/ma12010074