Defect States Determining Dynamic Trapping-Detrapping in β-Ga 2 O 3 Field-Effect Transistors

Year: 2019

Type: article

Abstract: β-Ga 2 O 3 is an intriguing material as a channel layer for the next generation high power transistors. To assess the device level effects of the traps in β-Ga 2 O 3 , the dynamic dispersion characteristics of a back-gated nanobelt β-Ga 2 O 3 field-effect transistor prepared by mechanical exfoliation from a bulk β-Ga 2 O 3 single crystal was investigated by the dependence of threshold voltage hysteresis on transistor transfer characteristics on the gate voltage ramp, pulsed current-voltage characteristics, and current deep level transient spectroscopy measurements. Current lag in the off-state was related to the presence of electron traps at E c -0.75 eV, which are also present in bulk crystals and ascribed to Fe impurities or native defects. In the on-state, drain current lag was caused by surface traps with levels at E c -(0.95–1.1) eV. Optimized passivation layers for β-Ga 2 O 3 are required to prevent the current collapse because the device performances are affected by the environmental molecules adsorbed on the surface. Our work can pave a way to mitigating the defect-related current collapse in β-Ga 2 O 3 electronic devices.

Source: ECS Journal of Solid State Science and Technology

DOI: 10.1149/2.0031907jss