Year: 2019
Type: article
Abstract: Antimony-telluride-based nanocomposite samples containing different weight fractions of graphite (Sb_2Te_3 + x % graphite, where x = 0.0, 0.5, 1.0, and 2.5%) are synthesized and studied. The samples are produced by a solid-state reaction with the use of a ball mill. X-ray diffraction measurements show that the Sb_2Te_3 phase is present in the nanocomposites. All of the diffraction peaks are identified as corresponding to the rhombohedral structure of symmetry $$R\bar {3}m$$ . No additional peaks related to graphite are observed because of its low content. Moreover, the X-ray data show the insolubility of graphite in Sb_2Te_3: the peaks related to Sb_2Te_3 remain unchanged upon the addition of graphite. The thermal conductivity, thermoelectric power, and resistivity of the samples are studied in the temperature range 80 K ≤ T ≤ 320 K. The thermal conductivity k of the nanocomposite decreases several times compared to the thermal conductivity of single-crystal Sb_2Te_3 and reaches k ≈ 0.95 W m^–1 K^–1 at x = 0.5%. The parameter k unsteadily depends on the content of graphite. The thermoelectric power of the nanocomposites with graphite at x = 1.0% is higher compared to that of nanostructured Sb_2Te_3.
Source: Физика и техника полупроводников
Authors: В.А. Кульбачинский, В.Г. Кытин, Д.А. Зиновьев, Н.В. Маслов, P. Singha, S. Das, A. Banerjee
Institutions: Lomonosov Moscow State University, University of Calcutta
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
OpenAlex ID: W2938130923