Core size does not affect blinking behavior of dye-doped Ag@SiO 2 core–shell nanoparticles for super-resolution microscopy

Year: 2020

Type: article

Abstract: ) shell on the self-blinking properties of these nanoparticles. Both core size and shell thickness were manipulated by altering the reaction time to determine core and shell effects on photoblinking. Size and shell thickness were investigated individually under both dry and hydrated conditions and were then doped with a 1 mM solution of Rhodamine 110 for analysis. We observed that the cores themselves are weakly luminescent and are responsible for the blinking observed in the fully-synthesized metal-enhanced fluorescence nanoparticles. There was no statistically significant difference in photoblinking behavior-both intensity and duty cycle-with decreasing core size. This observation was used to synthesize smaller nanoparticles ranging from approximately 93 nm to 110 nm as measured using dynamic light scattering. The blinking particles were localized via super-resolution microscopy and show single particle self-blinking behavior. As the core size did not impact blinking performance or intensity, the nanoparticles can instead be tuned for optimal size without sacrificing luminescence properties.

Source: RSC Advances

DOI: 10.1039/c9ra10421f

Authors: S. Thompson, Dimitri Pappas

Institution: Texas Tech University

Language: English

Topic: Gold and Silver Nanoparticles Synthesis and Applications

Subfield: Electronic, Optical and Magnetic Materials

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $1,042