Substrate-Dependent Exciton Diffusion and Annihilation in Chemically Treated MoS 2 and WS 2

Year: 2020

Type: article

Abstract: Atomically thin semiconductors such as monolayer MoS 2 and WS 2 exhibit nonlinear exciton–exciton annihilation at notably low excitation densities (below ∼10 excitons/μm 2 in exfoliated MoS 2 ). Here, we show that the density threshold at which annihilation occurs can be tuned by changing the underlying substrate. When the supporting substrate is changed from SiO 2 to Al 2 O 3 or SrTiO 3, the rate constant for second-order exciton–exciton annihilation, k XX [cm 2 /s], is reduced by 1 or 2 orders of magnitude, respectively. Using transient photoluminescence microscopy, we measure the effective room-temperature exciton diffusion coefficient in bis(trifluoromethane)sulfonimide-treated MoS 2 to be in the range D = 0.03–0.06 cm 2 /s, corresponding to a diffusion length of L D = 350 nm for an exciton lifetime of τ = 18 ns, which does not depend strongly on the substrate. We discuss possible mechanisms for the observed behavior, including substrate permittivity, long-range exciton–exciton or exciton–charge interactions, defect-mediated Auger recombination, and spatially inhomogeneous exciton populations arising from substrate-induced disorder. Exciton annihilation limits the overall efficiency of 2D semiconductor devices operating at high exciton densities; the ability to tune these interactions via the underlying substrate is an important step toward more efficient optoelectronic technologies featuring atomically thin materials.

Source: The Journal of Physical Chemistry C

DOI: 10.1021/acs.jpcc.0c04000