A novel Mn 4+ ‐activated far‐red Sr 2 MgWO 6 phosphor: synthesis, luminescence enhancement, and application prospect

Year: 2023

Type: article

Abstract: A novel far‐red emitting phosphor Sr 2 MgWO 6 : Mn 4+ was fabricated using high‐temperature solid‐state reaction. X‐ray diffraction patterns, scanning electron microscopy images, and photoluminescence excitation and photoluminescence spectra for this phosphor were analyzed in detail. The analysis revealed that its emission ranged from 600 to 800 nm and peaked at 699 nm, which was attributed to the 2 E g → 4 A 2g transition of Mn 4+ under 314 nm excitation. Moreover, we introduced rare‐earth Yb 3+ ions into the Sr 2 MgWO 6 :Mn 4+ to improve its far‐red emitting intensity. The photoluminescence (PL) intensity of the Yb 3+ co‐doped phosphor was three times higher than that of the single‐doped phosphor. Therefore charge compensation is an efficient approach to improving PL intensity. The phosphor emitted a far‐red light that resembled the pigments essential for plant growth in terms of the absorption spectrum. Therefore, the obtained phosphor, Sr 2 MgWO 6 :0.006Mn 4+ ,0.2Yb 3+ , had the potential to be a new type of far‐red luminescent powder for indoor plant growth LEDs.

Source: Luminescence

DOI: 10.1002/bio.4497

Authors: Xinyue Liu, Yamin Xu, Kang Cheng, Juling Long, Weichao Huang, Chaoyong Deng

Institution: Guizhou University

Language: English

Topic: Luminescence Properties of Advanced Materials

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: bronze

Funders: National Natural Science Foundation of China, Guizhou University

Award: G8995603038