Six‐principal‐component high‐entropy carbonitride aerogel thermal insulator: Theoretical and experimental studies

Year: 2024

Type: article

Abstract: A combined theoretical and experimental approach was used to investigate high‐entropy carbonitride. Density functional theory (DFT) calculations suggest that the [N]/([C]+[N]) ratio in (Ti 1/6 Cr 1/6 V 1/6 Mo 1/6 Nb 1/6 Ta 1/6 )(C 1− x N x ) affects its lattice thermal conductivity which could be decreased by 89% by increasing the ratio from 0 to 1/2. Moreover, a robust, flame‐retardant and high‐temperature resistant (Ti 1/6 Cr 1/6 V 1/6 Mo 1/6 Nb 1/6 Ta 1/6 )(C 0.64 N 0.36 ) high‐entropy carbonitride aerogel (6‐HECNA) was synthesized. It exhibited a porosity of 94.3%, a compressive strength of 0.9 MPa, and a good high‐temperature stability up to 1673 K. These properties, along with its outstanding fire‐retardancy, and low thermal conductivity (0.122 W·m −1 ·K −1 at 298 K), make it a promising candidate material for thermal insulation applications under harsh conditions.

Source: Journal of the American Ceramic Society

DOI: 10.1111/jace.20027

Authors: Lei Han, Yu Chen, Huifang Wang, Haijun Zhang, Shaowei Zhang

Institutions: University of Exeter, Wuhan University of Science and Technology, State Key Laboratory of Refractories and Metallurgy, Shanxi Institute of Technology

Language: English

Topic: Advanced ceramic materials synthesis

Subfield: Ceramics and Composites

Field: Materials Science

Domain: Physical Sciences

Open Access status: bronze

Funders: National Natural Science Foundation of China, China Postdoctoral Science Foundation, China Scholarship Council