Effect of Crevice Size on Crevice Corrosion of N80 Carbon Steel in CO2-Saturated NaCl-HAc Solution

Year: 2024

Type: article

Abstract: -saturated NaCl-HAc solution. The N80 carbon steel exhibits a high susceptibility to crevice corrosion in this environment, which can be initiated immediately without an induction period for specimens with crevice sizes of 100 μm, 300 μm, and 500 μm. Typically, crevice solutions become more acidic during crevice corrosion; however, in this study, the crevice solution became alkaline, resulting in galvanic corrosion between the inner and outer steel surfaces and leading to severe crevice corrosion. The pH levels of the crevice solution for specimens with 100 μm and 300 μm crevice sizes are similar, but both are notably higher than that of the specimen with a 500 μm crevice size. As a result, there is no significant difference in the crevice corrosion phenomenon between specimens with 100 μm and 300 μm crevice sizes, but it is more severe than in the specimen with a 500 μm crevice size.

Source: Materials

DOI: 10.3390/ma17164078

Authors: Pengfei Hu, Guangyi Cai, Yizhou Li

Institutions: Naval University of Engineering, Ocean University of China

Language: English

Topic: Corrosion Behavior and Inhibition

Subfield: Materials Chemistry

Field: Materials Science

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,955

Funder: National Natural Science Foundation of China