Abstract: Yttria stabilized zirconia (Y-TZP) ceramics with drastically reduced yttria content have been introduced by different manufacturers aiming at improving the damage tolerance of ceramic components. In this study an alumina doped 1.5Y-TZP was axially pressed, pressureless sintered in air at 1250–1400 °C for 2 h and characterized with respect to mechanical properties, microstructure and phase composition. The material exhibits a combination of high strength of 1000 MPa and a high toughness of 8.5–10 MPa√m. The measured fracture toughness is, however, extremely depending on measurement protocol. Direct crack length measurements overestimate toughness due to trapping effects. The initially purely tetragonal material has a high transformability of > 80 %, the transformation behavior is predominantly dilatoric, measured R-curve related toughness increments are in good agreement with transformation toughness increments derived from XRD data.
Source: Ceramics
Authors: Frank Kern, Bettina Osswald
Institution: University of Stuttgart
Language: English
Subfield: Ceramics and Composites
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,819
OpenAlex ID: W4401638798