Phase Equilibrium Investigations and Thermodynamic Study of the Y2O3-Ta2O5 System

Year: 2024

Type: article

Abstract: Two methods were used to investigate the Y 2 O 3 -Ta 2 O 5 system: the equilibration method, which covered temperatures from 1573 to 1973 K, and the DTA method, which reached up to 2473 K. Phase identification was carried out using x-ray diffraction and scanning electron microscopy with energy-dispersive x-ray spectroscopy (SEM/EDX). The temperature of the eutectic reaction, L → YTa 3 O 9 (P) + Ta 2 O 5 , was determined to be 2019 K, with the corresponding eutectic composition being 78 mol.% Ta 2 O 5 . The study presents evidence that contradicts the existence of the eutectic reaction L → YTaO 4 (T) + YTa 3 O 9 (P). Instead, it identifies a peritectic reaction L + YTaO 4 (T) → YTa 3 O 9 (P), which was observed at a temperature of around 2075 K. Additionally, the heat capacity of the YTa 3 O 9 (P) phase was measured using differential scanning calorimetry (DSC) over the temperature range from 240 to 1300 K. The results of this experimental investigation will lead to the development of a thermodynamic database for the Y 2 O 3 -Ta 2 O 5 system.

Source: Journal of Phase Equilibria and Diffusion

DOI: 10.1007/s11669-024-01137-4

Authors: M. Löffler, O. Fabrichnaya

Institution: TU Bergakademie Freiberg

Language: English

Topic: Metallurgical Processes and Thermodynamics

Subfield: Mechanical Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: hybrid

Estimated APC paid: $3,590

Funders: Deutsche Forschungsgemeinschaft, Technische Universität Bergakademie Freiberg