A study on properties of electroless Ni-B/MgB2 coatings on AZ91 magnesium alloy

Year: 2024
Type: article
Abstract: This study explores MgB 2 as a reinforcing agent in electroless deposition on AZ91 magnesium alloy substrates, evaluating its impact on coating properties. X-ray diffraction (XRD) analysis shows that the amorphous Ni-B coating masks initial magnesium peaks, while MgB 2 enhances MgB 2 O(OH) 6 , MgB 2 O 5 , MgO, and MgB 2x Oy oxide phases. SEM images illustrate morphological shifts from cauliflower-like Ni-B structures to dendritic and fibrous MgB 2 forms, with higher MgB 2 concentrations leading to granular structures with randomly oriented crystallites resembling platelets, indicating increased magnesium content. MgB 2 -reinforced Ni-B coatings exhibited higher hardness than the substrate but lower than as-deposited Ni-B. Friction coefficients initially decreased with Ni-B, increased significantly with 0.1 g MgB 2 , and decreased with higher reinforcements, remaining higher than substrate and as-deposited Ni-B. MgB 2 reinforcement increased surface roughness, causing local agglomerations in 0.5 g MgB 2 coatings. Contact angle measurements demonstrated enhanced hydrophilicity due to MgB 2 's superhydrophilic properties influenced by surface roughness. Antibacterial tests revealed superior properties with 0.1 g MgB 2 , suggesting a transition to MgB 2 -enriched structures and influencing material properties. While Ni-B/MgB 2 coatings improved over substrate, further research is needed to optimize parameters and understand stabilizer effects. These coatings also exhibited superhydrophilicity and promising antibacterial properties, suggesting potential in advanced surface engineering applications.
Source: Heliyon
DOI: 10.1016/j.heliyon.2024.e37029
Language: English
Open Access status: gold
Estimated APC paid: $2,100
OpenAlex ID: W4402035447
FWCI: 0.619
Cites: 133
Cited by: 6
Related to: 10