Probing room temperature indirect and minimum direct band gaps of h-BN

Year: 2024

Type: article

Abstract: Hexagonal boron nitride (h-BN) has attracted considerable interest as an ultrawide bandgap (UWBG) semiconductor. Experimental studies focused on the detailed near band-edge structure of h-BN at room temperature are still lacking. We report a direct experimental measurement of the near band-edge structure performed on h-BN quasi-bulk wafers via photocurrent excitation spectroscopy (PES). PES resolved the band-to-band transitions near M- and K-points in the Brillion zone (BZ), from which the room temperature indirect band gap of E g M K ∼6.02 eV, minimum direct bandgap at M-point of E g M = 6.36 eV and next lowest direct energy bandgap at K-point of E g K = 6.56 eV , have been simultaneously determined for the first time experimentally. The measured energy differences between K- and M-points in the conduction band minimum (CBM) and valence band maximum (VBM) are Δ E C M K = 0.54 eV and Δ E V M K = 0.34 eV, respectively, in good agreement with the calculation results. Significantly differing from its III-nitride wurtzite counterparts, in which only electrons and holes in the conduction and valence band extremes at the Γ-point are predominantly involved in the optical and transport processes, the results highlighted that charge carriers associated with both M- and K-valleys control to the optical excitation, recombination and charge transport processes in h-BN.

Source: Applied Physics Express

DOI: 10.35848/1882-0786/ad777a