Abstract: Intercalation is a powerful approach to customize the properties of layered materials such as titanium carbide (Ti3C2Tx) MXenes. Photonic curing, a novel technique employing intense pulsed light from a xenon flashlamp (≈280–1100 nm wavelength range), offers significant advantages over conventional annealing methods. The pulsed nature of photonic curing enables rapid quenching, which allows trapping of metastable states and the formation of unique nanostructures. Herein, this work reports on the ion exchange intercalation of Ti3C2Tx MXenes with aminopropyl terminated polydimethylsiloxane (amino‐PDMS) and the subsequent application of photonic curing to study pyrolysis of intercalated PDMS. The results showed an increase in the interlayer spacing (d‐spacing) of Ti3C2Tx from 1 to 13.5 nm for the 5 kg mol−1 amino‐PDMS (5K‐PDMS) intercalant. After photonic curing, the intercalated PDMS is converted into SiOx or silicon oxycarbide, and the d‐spacing decreased from 13.5 to 11 nm. Furthermore, curing the intercalated MXenes under controlled pressure in different gas environments, this work observes the conversion of PDMS to silicon carbide on the surface of MXenes layers. This study demonstrates the potential of photonic curing as a promising approach for cost‐effective, instantaneous, and scalable synthesis of customizable layered materials with precise control over the nanostructure within the layers.
Source: Advanced Materials Interfaces
Institution: Tulane University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,100
Funder: Louisiana Board of Regents
Award: G5646080024
OpenAlex ID: W4402282820