Revealing the microstructural evolution and mechanical response of repaired Fe–Cr–Si based alloy by directed energy deposition
Year: 2024
Type: article
Abstract: This study investigates the microstructure and mechanical properties of wear-resistant hardfacing structures fabricated on an AISI 1045 carbon steel substrate using a specially designed Fe–Cr based powder for directed energy deposition (DED). Electron backscatter diffraction (EBSD) analysis reveals that the texture predominantly consists of cube rotated {001}<110> and cube {001}<110> textures, in addition to weaker Brass {112}<111> texture components. These textures contribute to the random orientations of martensitic grains and facilitate the tracing of austenite reconstruction. Notably, the as-printed samples exhibited superior yield strength (999.4 ± 86.3 MPa) and ductility (9.6 ± 2.6%) along the build direction (BD), compared to conventional samples, which demonstrated a tensile strength of 790 MPa and ductility of 2%. This improvement is primarily attributed to the hardening effects associated with a low volume fraction of retained austenite and the precipitation of Cr carbides . Comprehensive mechanical response, nanoindentation hardness profile across the interface, and microstructural analyses were conducted to confirm the feasibility of using a Fe-based hardfacing alloy for DED. The findings underscore the outstanding balance of strength and ductility exhibited by as-printed hardfacing alloy, further enhanced by its high printability, highlighting its potential in producing wear-resistant structures for repair applications.
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,430
Awards: G3178273089, G5477784756
OpenAlex ID: W4402338947