Experimental investigation on the residual strength of concrete under the multi-factor coupling action of chloride penetration, freeze-thaw, and fatigue effect
Year: 2024
Type: article
Abstract: With the ongoing process of globalization and the rapid expansion of the global economy, the proliferation of coastal constructions and infrastructures has witnessed a notable surge. These structures often encounter a confluence of environmental stressors in practical engineering, including cyclic fatigue loading , chloride salt erosion, and freeze-thaw cycles. These synergistic factors accelerate concrete’s failure, resulting in accelerated deterioration and significantly reduced durability. A comprehensive understanding of the damage characteristics of concrete materials in offshore environments, under the multi-factor coupled action of freeze-thaw phenomena, along with an assessment of their residual strength , is crucial for the development of relevant structural analysis and lifetime prediction models. To address this, twenty-seven dedicated specimens were designed and fabricated for this investigation. They were employed to scrutinize the residual strength of concrete under the combined influences of fatigue, freeze-thaw, and chloride penetration . Nine distinct multi-factor coupling actions were meticulously devised and characterized by different parameters. Following the multi-factor coupling action, tests were conducted to assess the residual flexural and compressive strengths , as well as the chloride ion content near the specimen edges. The findings revealed a substantial negative correlation between the residual flexural and compressive strengths with both the number of freeze-thaw cycles and fatigue loading iterations. In contrast, chloride ion concentration and the stress level of fatigue loading (stress ratio: 0.1–0.3) exhibited a comparatively marginal influence. Despite the relatively short test duration, it was evident that both freeze-thaw cycles and fatigue loading exerted a discernible promotional effect on chloride ion ingress in the concrete of the specimens.
Language: English
Subfield: Civil and Structural Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,110
OpenAlex ID: W4402404789