Enhancing tensile and fatigue properties of high-speed-extruded Mg–5Bi–3Al alloy using non-homogenized extrusion billet
Year: 2024
Type: article
Abstract: This study aims to improve the tensile and high-cycle fatigue properties of a high-speed-extruded BA53 (Mg–5Bi–3Al, wt.%) alloy using a non-homogenized extrusion billet. Homogenization treatment of the BA53 billet leads to a significant reduction in the area fraction of Mg 3 Bi 2 particles from 12.9% to 2.5% and an increase in the average grain size from 142 to 189 μm. The BA53 material produced via the high-speed extrusion of the cast billet (Cast-E) and that produced via the high-speed extrusion of the homogenized billet (Homo-E) both exhibit a fully recrystallized microstructure. However, Cast-E has a finer grain size and many more Mg 3 Bi 2 particles than Homo-E. In addition, the tensile yield strength and elongation of Cast-E are 211 MPa and 9.4%, respectively, higher than those of Homo-E (198 MPa and 7.9%). This higher strength is attributed to the strengthening effects of the higher number of Mg 3 Bi 2 particles, the finer grain size, and the higher internal strain energy. The fatigue limit for Cast-E is 100 MPa, which is 25% higher than that of Homo-E (80 MPa). This occurs because the numerous fine Mg 3 Bi 2 particles in Cast-E inhibit the formation of persistent slip bands on the specimen surface and impede crack propagation. This study proposes a new manufacturing process that does not require billet homogenization, thus simultaneously improving the productivity of the extrusion process and the tensile and fatigue properties of the resulting BA53 alloy.
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,430
Awards: G2317512543, G6197896602
OpenAlex ID: W4402538233