Influence of deep-sea hydrostatic pressure on the tribocorrosion behavior and mechanism of La2O3–TiB2–Ni coating
Year: 2024
Type: article
Abstract: To understand the tribocorrosion mechanism of TiB 2 –Ni coating doped with La 2 O 3 in the deep ocean, the wear and corrosion test of La 2 O 3 –TiB 2 –Ni under various hydrostatic pressures was conducted and discussed in 3.5 wt % NaCl solution. The results indicate that the tribocorrosion mechanism of the La 2 O 3 –TiB 2 –Ni coating transitions from abrasive wear with corrosion under 0.1 MPa to abrasive wear with corrosion and adhesive wear under high hydrostatic pressure. The La 2 O 3 –TiB 2 –Ni coating shows significant enhancements in wear resistance and anti-friction properties compared to the TiB 2 –Ni coating. As the hydrostatic pressure increases from 0.1 MPa to 30 MPa, the self-corrosion current density experiences an approximate increase of 43.6 μA/cm 2 .
Authors: Zhengyi Li, botai Su, Pengwei Ren, Lei Wen, Dongbai Sun
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,430
Awards: G638032169, G7965460221
OpenAlex ID: W4402564739