Colloidal route towards sodium ionic conductor (NASICON) 3D complex solid electrolyte structures fabricated by direct ink writing (DIW)
Year: 2024
Type: article
Abstract: Progressing towards a sustainable energy model, safer new generation high-performance energy storage devices with large energy density and power are needed. In this sense, the improvement in terms of efficiency and sustainability has led to the interest in solid-state batteries (SSBs). Lately, sodium-ion batteries (SIBs) have become an emerging alternative due to the abundance of raw materials, low cost, and improvements in terms of fast sodium-ion conductor solid electrolytes (SCSEs). Among all the SCSEs, the sodium superionic conductor (NASICON) type electrolyte is one of the most well-known electrolytes, being widely developed in terms of synthesis and materials. However, the processing and manufacturing of these electrolytes have gone almost unnoticed, without considering that well-designed structures of electrodes/electrolytes are the bridge toward turning advanced energy materials into high-performance devices. This work presents the fabrication of 3D complex structures based on NASICON sodium solid electrolytes, obtained for the first time by direct ink writing (DIW). Through a colloidal route, fine NASICON phase powder with high pureness was prepared, enabling the manufacturing of intricate NASICON-printed electrolytes in a one-step fabrication process. By optimizing the ink, a dense electrolyte layer, acting as an ionic conductor and separator, was inserted between two complex porous pattern layers obtaining a device with a total height below 1.15 mm. Further, the densification of the 3D electrolyte was enhanced, reaching high ionic conductivities at room temperature (3.10 −4 S cm −1 ). Thus, a high-performance sodium ion conductor NASICON solid electrolyte with shorter diffusion pathways and larger interfacial surface areas between electrode/electrolyte was obtained, improving the overall electrochemical performance of the device by a 3D layer-by-layer design. • Through a colloidal approach highly homogenized green NASICON powder mixture is efficiently obtained. • Fine (>36 μm) NASICON powder for DIW is obtained. • The rheological properties of carboxymethyl cellulose (CMC) – NASICON inks are optimized. • Complex 3-layer 3D solid electrolyte is printed in a one-step fabrication process. • Printed 3D NASICON solid electrolyte achieves high ionic conductivity of 3 × 10 −4 S cm −1 at room temperature.
Source: Open Ceramics
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,000
OpenAlex ID: W4402635718