Investigation of the microstructure and tribological properties of laser cladding 5%Ti3SiC2 reinforced Co-based composite coatings under different loads over the wide temperature range
Year: 2024
Type: article
Abstract: In order to improve the mechanical properties of SUS 304 in practical engineering application, Co-5%Ti 3 SiC 2 coating was successfully prepared on SUS 304 by laser technology. The microstructure of Co-5%Ti 3 SiC 2 coating was characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and X-ray diffractometer (XRD) to evaluate the tribological properties in detail. The relevant wear mechanism of the substrate and Co-5%Ti 3 SiC 2 coating under different loads (2, 5 and 8 N) in isothermal tribological experiments (25 and 600 °C) were systematically explored. The results show that the Co-5%Ti 3 SiC 2 coating is mainly composed of continuous matrix γ-Co solid solution, ceramic Fe 2 C, Cr 7 C 3 and TiC, and lubricating phase Ti 3 SiC 2 . The average micro-hardness of Co-5%Ti 3 SiC 2 coating is 358.61 HV 0.5 , which is significantly higher than that of SUS 304 (239.32 HV 0.5 ). In all isothermal tribological experiments, the wear rate of Co-5%Ti 3 SiC 2 coating decreases with the increase of load, and its coefficient of friction (COF) also decreases with the increase of load. • The Co-Ti 3 SiC 2 composite coatings were successfully prepared on 304 stainless steel by laser cladding. •The MAX phase Ti 3 SiC 2 elevated the wear resistance of composite coatings under different loads over the wide temperature range. •The MAX phase Ti 3 SiC 2 played lubrication and protection roles in the coatings, which improve the tribological properties. •The wear mechanisms were investigated from the morphology of surface and wear affected zone respectively.
Source: Results in Engineering
Authors: Zhi-shen Gao, Jingkai Xue, Chun-sheng Ouyang, ying-she Luo, Ke Ding, Hong-shuo Guo, Gang Yan
Language: English
Subfield: Mechanical Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,490
OpenAlex ID: W4403378387