Honeycomb Cell Structures Formed in Drop-Casting CNT Films for Highly Efficient Solar Absorber Applications
Year: 2024
Type: article
Abstract: This study investigates the process of multi-walled carbon nanotube (MWCNT) coatings to enhance the lamp heating temperature for solar thermal absorption applications. The primary focus is studying the effects of self-organized honeycomb structures of CNTs formed on silicon substrates on different cell area ratios (CAR). The drop-casting process developed honeycomb-structured MWCNT-coated absorbers with varying CAR values ranging from ~ 60% to 17%. The optical properties were investigated within the visible (400-800 nm) and near-infrared (934-1651nm) wavelength ranges. Although fully coated MWCNT absorbers showed the lowest reflectance, honeycomb structures with a ~ 17% CAR achieved high-temperature absorption. These structures maintained 8.4% reflectance at 550 nm while dramatically increasing infrared reflection to 80.5% at 1321 nm. The performance of solar thermal was assessed throughout a range of irradiance intensities, from 0.04 W/cm² to 0.39 W/cm². The honeycomb structure with a ~17% CAR value consistently performed better than other structures by reaching the highest absorption temperatures (ranging from 52.5°C to 285.5°C) across all measured intensities. A direct correlation was observed between the reflection ratio (visible: 550 nm / infrared: 1321 nm) and temperature absorption efficiency, where lower reflection ratios were associated with higher temperature absorption. This study highlights the significant potential for the large-scale production of cost-effective solar thermal absorbers through the application of optimized honeycomb-structured absorbers coated with MWCNTs. These contributions enhance solar energy efficiency for applications in water heating and purification, thereby promoting sustainable development.
Source: Nanomaterials
DOI: 10.3390/nano14201633
Authors: Saiful Islam, Hiroshi Furuta
Institution: Kochi University of Technology
Language: English
Subfield: Civil and Structural Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $3,296
OpenAlex ID: W4403379958