Unraveling Asymmetric Electrochemical Kinetics in Low-Mass-Loading LiNi1/3Mn1/3Co1/3O2 (NMC111) Li-Metal All-Solid-State Batteries

Year: 2024

Type: article

Abstract: In this study, we fabricated a Li-metal all-solid-state battery (ASSB) with a low mass loading of NMC111 cathode electrode, enabling a sensitive evaluation of interfacial electrochemical reactions and their impact on battery performance, using Li1.3Al0.3Ti1.7(PO4)3 (LATP) as the solid electrolyte. The electrochemical behavior of the battery was analyzed to understand how the solid electrolyte influences charge storage mechanisms and Li-ion transport at the electrolyte/electrode interface. Cyclic voltammetry (CV) measurements revealed the b-values of 0.76 and 0.58, indicating asymmetry in the charge storage process. A diffusion coefficient of 1.5 × 10−9 cm2⋅s−1 (oxidation) was significantly lower compared to Li-NMC111 batteries with liquid electrolytes, 1.6 × 10−8cm2⋅s−1 (oxidation), suggesting that the asymmetric charge storage mechanisms are closely linked to reduced ionic transport and increased interfacial resistance in the solid electrolyte. This reduced Li-ion diffusivity, along with the formation of space charge layers at the electrode/electrolyte interface, contributes to the observed asymmetry in charge and discharge processes and limits the rate capability of the solid-state battery, particularly at high charging rates, compared to its liquid electrolyte counterpart.

Source: Materials

DOI: 10.3390/ma17205014

Author: Byoung-Nam Park

Institution: Hongik University

Language: English

Topic: Advanced Battery Materials and Technologies

Subfield: Electrical and Electronic Engineering

Field: Engineering

Domain: Physical Sciences

SDG: Affordable and clean energy

Open Access status: gold

Estimated APC paid: $2,955