Investigation of fracture mechanical properties of a brass alloy with microstructural variations
Year: 2024
Type: article
Abstract: This study investigates the effect of microstructural variations on the mechanical properties of CuZn35Mn2Al1Fe1-C-GS brass alloy. Specimens taken from positions with different cooling rates in a large cast component exhibit coarse-grained (approximately 5 mm) and fine-grained (approximately 1 mm) microstructures. Fine-grained samples demonstrate at least a 7% increase in Ultimate Tensile Strength (UTS) and up to a 33% higher long crack threshold Δ K th,lc . Hardness measurements are similar between microstructures. The NASGRO model and cyclic R-curve are applied to fit crack propagation data, and fractographic analysis reveals distinct fracture mechanisms. The results indicate that a fine-grained microstructure enhances tensile strength and crack resistance, providing valuable insights for the design and maintenance of heavy machinery components made from cast brass. • Cyclic fracture mechanical characterization of CuZn35Mn2Al1Fe1-C-GS brass. • Fine-grained microstructure enhances tensile strength by at least 7%. • Cyclic R-curves indicate a +33% rise in alternating Δ K th,lc for fine-grain brass. • Provides NASGRO and cyclic crack resistance fit parameters for two microstructures. • Fracture analysis shows reduced intercrystalline proportion in coarse-grain samples.
Source: Engineering Fracture Mechanics
Institution: Montanuniversität Leoben
Language: English
Subfield: Mechanics of Materials
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,000
OpenAlex ID: W4403633854