Effect of Curing Time and Ferric Chloride on a Copper Concentrate with a High Arsenic Content

Year: 2024

Type: article

Abstract: As a result of changes in copper mineralogy, various treatment options for copper sulfides have been explored, including pretreatment processes aimed at enhancing material permeability and improving the dissolution of valuable minerals. Despite its significance, this topic has only recently gained attention. In this research, a copper concentrate with a high arsenic content was studied, with enargite (Cu3AsS4) as the main mineral phase. The objective was to evaluate the effect of pretreatment on copper extraction efficiency prior to leaching. Three key variables were investigated: curing time (0, 5, 10, and 15 days), H2SO4 dosage (0, 70, 140, and 210 kg/t), and FeCl3 concentration (0, 0.5, 1, and 1.5 M). The sample was characterized both before and after pretreatment, revealing the formation of new species such as CuSO4·5H2O and Cu2Cl(OH)3 under optimal conditions of 15 days curing time, 70 kg/t of H2SO4, and 1 M FeCl3. Copper extraction solely through curing reached 20.79%. The analysis suggests that curing time is the most influential factor in the process, accounting for 46% of the overall contribution. In comparison, sulfuric acid and ferric chloride contribute less, with 20% and 10% contributions, respectively.

Source: Minerals

DOI: 10.3390/min14111063

Authors: Víctor Quezada, Stephano Zepeda, Oscar Benavente, María Cecilia Hernández, Evelyn Melo

Institution: Universidad Católica del Norte

Language: English

Topic: Metal Extraction and Bioleaching

Subfield: Biomedical Engineering

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,728

Funder: Universidad Católica del Norte