Incorporation of Thioacetate Pendants on a Polyalkenamer Enables High Extensibility

Year: 2024

Type: article

Abstract: This study focuses on functionalizing polycyclooctene (PCOE) with thioacetate groups using thiol–ene click chemistry. The ethylene thioacetate (EVSA) copolymers produced vary in thioacetate incorporation (4–25 mol %) via a controlled semibatch addition technique with AIBN dosing. Copolymers with 4–14 mol % thioacetate are semicrystalline, while those with 20–25 mol % are amorphous. Increased functionalization correlates with decreased crystallinity and increased stretchability, with the highest functionalization (25 mol %) showing a modulus of 0.045 MPa and 2000% elongation at break. This behavior is due to the pseudoprecise functionalization of the thioacetate pendants and intrinsic cross-linking that occurs during melt processing. Broadband dielectric spectroscopy (BDS) indicates a low activation energy barrier (16 kJ/mol for the β process), suggesting potential self-healing applications.

Source: Macromolecules

DOI: 10.1021/acs.macromol.4c02110