Probing pyrolysis conversion of separator from spent lithium-ion batteries: Thermal behavior, kinetics, evolved gas analysis and aspen plus modeling

Year: 2024

Type: article

Abstract: The exponential growth in the consumption of lithium-ion batteries (LIBs) has resulted in a concomitant increase in the spent LIBs. Multi-component recycling is a highly desirable and beneficial process, yet the separator component remains overlooked. This study examined the thermal behavior, kinetics, thermodynamics, and evolved products of separator pyrolysis in N 2 and CO 2 atmospheres. Furthermore, the conversion was modeled using Aspen Plus and a sensitivity analysis was conducted to investigate the impact of varying operating conditions. The findings indicated that the whole degradation process could be divided into three stages: below 200 °C, 200–550 °C and 550–900 °C. The evolved products at peak temperatures of 485 °C in N 2 and 500 °C in CO 2 were composed of olefins and alkanes. The average apparent activation energy values were determined to be 222.78 kJ mol −1 and 159.36 kJ mol −1 in the N 2 and CO 2 atmospheres, respectively. Thermodynamic analysis indicated that the separator decomposition was an endothermic and non-spontaneous process. Aspen Plus modeling results were in agreement with the experimental data. The sensitivity analysis revealed that an increase in temperature lead to an increased content of lighter compounds (≤C9) and a decrease in the proportion of heavier compounds (>C10) in the pyrolysis products.

Source: Case Studies in Thermal Engineering

DOI: 10.1016/j.csite.2024.105342