TiO2 and down-conversion phosphors to enhance UV protection of solar cells
Year: 2024
Type: article
Abstract: In recent years, demand for solar generators for LEO (Low Earth Orbit) applications has been growing, and much research has focused on the use of less expensive and thinner (<90 μm). silicon-based solar cells that can be integrated on flexible Photovoltaic Assemblies (PVAs). These solar cells must be protected from space UV radiations and also withstand more than 50,000 thermal cycles in LEO. The solution advocated here involves the incorporation of UV-absorbing particles into a spatial polymer, combined with lanthanide ions based inorganic phosphors (Y 2 O 3 :Eu 3+ and Y 2 O 2 S:Eu 3+ ) to achieve the down-conversion process. Embedded into a silicone-based polymer matrix with a thickness close to 100 μm, these particles are then deposited on 180 μm thick Ga-doped heterojunction silicon cells (30x30 mm 2 ). UV tests are carried out on ONERA's SEMIRAMIS platform at two doses: 425 esh and 1005 esh. A series of 1000 thermal cycles is carried out at the CEA. The first spatial UV analysis revealed a maximum loss of almost 5 % in short-circuit current (Isc) for PV devices after 1005 esh. Comparing results in open circuit voltage (Voc), the bare cell degrades as the dose increases (−2 % at 425 esh and −5 % at 1005 esh). One positive point is that the addition of TiO 2 particles protects the solar cell. These initial results point out that it is possible to produce a protective coating to limit the effects of degradation of Silicon cells under space UV flux, with a focus on producing flexible PVAs. • Space UV resistant frontsheets for photovoltaic arrays based on Silicon solar cells. • Reduced degradation electrical performance after UV exposure with Ti0 2 particles. • Evaluation under space UV radiations of down-converters and absorbing particles. • Behaviors of UV resistant frontsheets with Low Earth Orbit thermal constraints.
Institutions: Commissariat à l'Énergie Atomique et aux Énergies Alternatives, Laboratoire d’Innovation pour les Technologies des Énergies Nouvelles et les nanomatériaux, Institut National de l'Énergie Solaire, Centre National de la Recherche Scientifique, Université Clermont Auvergne, Institut de Chimie de Clermont-Ferrand, Clermont Auvergne INP, Centre National d'Études Spatiales
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,430
Award: G7434054661
OpenAlex ID: W4404142959