Untypical tuneable emission activated by NIR radiation observed in gadolinium borate nanomaterials doped with Yb3+, Ho3+ and Ce3+ ions
Year: 2024
Type: article
Abstract: New luminescent nanoparticles with adjustable emission properties were synthesized via a hydrothermal method to investigate the effect of Ce3+ concentration on the tuneable emission properties of Yb3+/Ho3+ co-doped gadolinium borates. The synthesized samples' comprehensive structural and morphological analysis was conducted utilizing X-ray diffraction and transmission electron microscopy. To obtain highly crystalline nanoparticles GdBO3:Yb3+/Ho3+/Ce3+ characterized by intense and bright emission, they were annealed at 525°C and 925°C. Under the excitation of 972 nm, the tunable yellow to green up-conversion emission was observed, while the Ce3+ concentration increased. This change correlated with a difference in the correlated color temperature from 4345K to 5442K, respectively. The untypical changes observed in the red-to-green (R/G) ratio, displaying a declining trend contrary to conventional expectations, allowed for the proposed mechanism for understanding their UC luminescence properties. The results obtained indicate that the Ce3+ doped GdBO3:Yb3+/Ho3+ nanoparticles demonstrate high application potential for anti-counterfeiting.
Source: Scientific Reports
Authors: Agata Szczeszak, Justyna Czajka
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,590
Funder: Narodowe Centrum Badań i Rozwoju
OpenAlex ID: W4404240854