Study on mechanical degradation of Ferrite/ martensite and austenitic steels in high-temperature supercritical carbon dioxide environment

Year: 2024

Type: article

Abstract: • The mechanical degradation mechanism of T91 and 316NG steels in S-CO 2 were investigated by slow strain rate tensile tests. • First-principles calculations were employed to examine the adsorption and dissociation process of CO 2 on the surfaces. • A composite failure mode with intergranular brittle fracture and ductile fracture was observed for 316NG at 600 o C. • CO 2 could spontaneously dissociate into CO and O, and the spontaneously and partially dissociated O atoms exhibited a strong interaction with Cr. The mechanical degradation mechanism of T91 ferrite/martensite steel at 500 °C and 316NG austenitic steel at both 500 °C and 600 °C in supercritical carbon dioxide were investigated in detail by slow strain rate tensile tests and first-principles calculations of the adsorption and dissociation of CO 2 . In high-temperature CO 2 atmosphere, CO 2 could spontaneously dissociate into CO and O, and the spontaneously and partially dissociated O atoms exhibited a strong interaction with Cr. As the temperature was increased to 600 °C, the partial dissociation of CO 2 occurred more rapidly and the ultimate tensile strength and total elongation of 316NG steel decreased significantly as well. Furthermore, a composite failure mode with intergranular brittle fracture and ductile fracture was investigated.

Source: Materials & Design

DOI: 10.1016/j.matdes.2024.113455