Arctic temperature effects on the mechanical properties and failure modes of photopolymer resin for sandwich composite core' materials
Year: 2024
Type: article
Abstract: The increased marine activity in the Arctic Circle presents significant challenges for naval structures operating in extreme conditions, such as temperatures as low as -60 °C (Arctic temperature, AT). This study uniquely investigates the potential of Formlabs' “Durable resin” as a core material for sandwich composites. It focuses explicitly on its mechanical response under these extreme Arctic conditions, a largely unexplored area in current materials research. Durable resin's quasi-static tensile, flexural, and compressive behaviors were tested at both room temperature (RT) and AT. Finite element models were developed to explain observed failure mechanisms. At AT, the resin showed isotropic behavior with notable improvements, including a 318% increase in tensile modulus, 322% rise in ultimate tensile strength, 450% increase in flexural modulus, and 460% improvement in compressive modulus, though strain at failure decreased. Failure modes varied by temperature: tensile and flexural fractures consistently occurred at the midsection, while compressive samples at AT failed via axial splitting, compared to barreling at RT. This study's findings contribute to the foundational understanding needed to develop materials that endure extreme Arctic environments, underscoring the promise of Durable resin for Arctic exploration despite its reduced ductility under AT conditions. • Stereolithography (SLA) additive-manufactured specimens exhibited isotropic properties. • The quasi-static strength and stiffness increased under Arctic temperature. • The samples exhibited embrittlement at Arctic temperatures. • The SLA specimens exhibited foam cell-like behavior under compression. • The samples exhibited brittle failure at Arctic temperatures.
Source: Results in Engineering
Authors: Zackery Nieto, Alejandra G. Castellanos
Institution: The University of Texas at El Paso
Language: English
Subfield: Automotive Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $1,490
OpenAlex ID: W4404420759