Insight into the Mechanical Properties and Microstructure of Recycled Aggregate Concrete Containing Carbon Fibers and Nano-SiO2

Year: 2024

Type: article

Abstract: (NS) to promote the optimal utilization of RAC. The mechanical properties of the RAC were enhanced by both single and hybrid additions of CFs and NS, and the hybrid addition had a better strengthening effect. From the experimental results, it was found that the addition of CFs could increase the 28 d compressive strength and splitting strength of the RAC by 9.05% and 22.36%, respectively. The hybrid CFs and NS were more conducive to improving the mechanical properties of the RAC, and the enhancement effect increased first and then decreased with an increase in the NS content. The optimal content of NS was 0.8 wt%, which increased the 28 d compressive strength and splitting strength of the RAC by 20.51% and 14.53%, respectively. The microstructure results indicated that the addition of CFs had little effect on the optimized pore structure of the RAC, but the crack inhibition action of the CFs could improve the mechanical properties of the RAC. The addition of NS reduced the content of CH and facilitated the formation of more (C-S-H) gel. The hydrated calcium silicate (C-S-H) gel significantly decreased the porosity and transformed harmful capillary pores and harmful pores into harmless capillary pores and gel pores, thus improving the mechanical properties of the RAC. Therefore, the use of hybrid CFs and NS was more conducive to enhancing the performance of RAC for building materials.

Source: Materials

DOI: 10.3390/ma17225633

Authors: Tong Xing, Feng shao Zhang, Lei Guan

Institutions: Jilin Engineering Vocational College, Shaanxi Railway Institute

Language: English

Topic: Recycled Aggregate Concrete Performance

Subfield: Building and Construction

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $2,955