Caries affected Dentin biomodification using Bromelain, Riboflavin photosensitizer via UVA, and Chitosan Nanoparticles on shear bond strength and microleakage scores: A SEM evaluation

Year: 2024

Type: article

Abstract: • The lowest microleakage score and highest bond integrity were observed in Group 2 samples treated with Bromelain. • The results indicated that samples treated with Bromelain attained the highest resin permeation with grade 3. • The length of resin tags in Group 2 specimens treated with Bromelain was found to be the highest. Assessment of the impact of different dentin bio-modifiers i.e., Bromelain, Riboflavin photosensitizer (RFP/Ultraviolet-A), and Chitosan nanoparticles (CHNPs) on the shear bond strength (SBS) and microleakage of composite bonded to acid etched carious affected dentin (CAD). Sixty-four human molars in which carious lesions extend till the middle third of the dentin were included. The infected dentin was removed and CAD was exposed. All specimens were categorized into four groups based on the application of dentin bio-modifier ( n = 16) Group 1 (No dentin modifier), Group 2 (Bromelain), Group 3 (RFP/UVA), and Group 4 (CHNPs). Dental adhesive application and composite buildup were performed. A dye penetration test was used to assess marginal leakage. Resin CAD interface assessment was performed using SEM. For SBS and failure pattern analysis, a universal testing machine and stereomicroscope were used respectively. One-way ANOVA followed by Bonferroni's posthoc test was employed to analyze the differences among various groups (p ≤ 0.05) The lowest microleakage (13.27 ± 0.10) and highest SBS (11.64 ± 0.16 MPa) were observed in Group 2 (Bromelain). However, the maximum values of marginal leakage (37.21 ± 0.21) and minimum SBS (7.34 ± 0.07 MPa) were detected in Group 1 samples. The length of resin tags in the Group 2 specimens (Bromelain) was found to be the highest (102.11 ± 5.12 μm) . However, Group 1 (No modifier) exhibited the lowest resin tag length (50.45 ± 2.37 μm). Caries-affected dentin modified with Bromelain resulted in satisfactory SBS with minimal microleakage scores. Chitosan nanoparticles and RFP/Ultraviolet-A also presented better outcomes in terms of microleakage and SBS than the control.

Source: Photodiagnosis and Photodynamic Therapy

DOI: 10.1016/j.pdpdt.2024.104419

Authors: Khold Alahdal, Ahmed Maawadh, Laila AlDeeb, Thamer Almohareb, Ahoud S Alshamrani, Ali Alrahlah

Institution: King Saud University

Language: English

Topic: Dental materials and restorations

Subfield: Orthodontics

Field: Dentistry

Domain: Health Sciences

SDG: Good health and well-being

Open Access status: gold

Estimated APC paid: $2,450