Measurement and analysis of residual stress of multilayer carbon fiber laminate based on incremental drilling method

Year: 2024

Type: article

Abstract: In the automotive and aerospace industries, carbon fiber is widely used in structures such as chassis and wings due to its lightweight and excellent mechanical properties, and the residual stresses are crucial for product design. In this paper, six kinds of carbon fiber laminates with different layup directions are investigated by using the integral method, and the calibration coefficient matrix is numerically solved by using ABAQUS finite element software, and the effects of laminate direction and incremental step on the three-direction residual stresses are experimentally analyzed. The residual stresses in different oriented layers were predicted by classical lamination theory (CLT), and the longitudinal, transverse and in-plane shear stresses were compared by combining incremental drilling experiments with calibration factors. The results showed that the ply with [ 45 / 90 / − 45 / 0 / 45 / 90 / − 45 / 0 ] laminate had the best performance,the difference between theoretical and experimental values for σ x was 0 . 421 MPa . The maximum τ x y measurement was 1 . 7103 MPa , with a maximum percentage error of 25.3%. The maximum difference for σ y was 0 . 7306 MPa . These findings indicate that the method is more accurate in predicting the residual stresses in the first four layers of composite material. This provides important theoretical and experimental support for the optimal design of composites. • Incremental drilling method measures residual stress in the first four laminate layers with an error below 25%. • The [ 45 / 90 / − 45 / 0 / 45 / 90 / − 45 / 0 ] laminate had the smallest residual stress values. • Differences between theoretical and experimental values for σ x , σ y , τ x y were 0 . 421 MPa , 0 . 7306 MPa , and 1 . 7103 MPa . • Measured residual stress of incremental drilling method agrees well with classical laminate theory.

Source: Polymer Testing

DOI: 10.1016/j.polymertesting.2024.108646

Authors: Keming Zhang, Cong Yu, Chunhai Chen

Institution: University of Shanghai for Science and Technology

Language: English

Topic: Mechanical Behavior of Composites

Subfield: Mechanics of Materials

Field: Engineering

Domain: Physical Sciences

Open Access status: gold

Estimated APC paid: $2,580

Funders: National Engineering and Research Center for Commercial Aircraft Manufacturing, National Natural Science Foundation of China