Work

Development of filler-free and ambient-cured fly ash based geopolymer brick utilizing low molar concentration of activating solution

Year: 2024

Type: article

Abstract: In this study, an effort has been undertaken to develop geopolymer bricks (GPB) using fly ash and an activating solution without the addition of any filler material. The primary objective is to establish the optimum mix ratio with the lowest possible concentration of sodium hydroxide (NaOH) in activating solution when mixed with fly ash, resulting in the GPB having compressive strength exceeding 10 MPa and water absorption below 20 % (Class-10 bricks). To achieve this objective, different activating solutions consisting of NaOH, a combination of NaOH and sodium silicate (Na 2 SiO 3 ), and a combination of NaOH, Na 2 SiO 3 , and additional water were used. The samples underwent ambient curing until the age of testing. The X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS) analyses examined the microstructural behavior of the GPB. Experimental results indicated that the compressive strength of 18 MPa and water absorption of 16.49 % was achieved when 2 M NaOH with Na 2 SiO 3 and 5 % extra water were used to activate fly ash. Microstructural analysis revealed that the undissolved fly ash particles served as filler material, while the dissolved fly ash helped in the synthesis of cementitious material. The performance of these bricks was found to be equivalent to that of the traditionally available burnt clay bricks. • Geopolymer bricks were made without fillers and ambient cured. • The minimum concentration of NaOH in the activating solution was 2 M. • Bricks had similar strength and absorption properties as clay bricks. • Microstructural analysis of brick was carried out. • These lightweight bricks may replace the traditional class 12.5 clay bricks.

Source: Case Studies in Construction Materials

DOI: 10.1016/j.cscm.2024.e04032

Authors: Sher Bahadur Singh, Pabitra Ranjan Maiti, Supriya Mohanty

Institution: Indian Institute of Technology BHU

Language: English

Topic: Concrete and Cement Materials Research

Subfield: Civil and Structural Engineering

Field: Engineering

Domain: Physical Sciences

SDGs: Responsible consumption and production, Industry, innovation and infrastructure

Open Access status: gold

Estimated APC paid: $2,110