Investigation of solution-processed tungsten disulfide as switching layer in flexible resistive memory devices for performance and stability
Year: 2024
Type: article
Abstract: Solution-processed tungsten disulfide (WS 2 ) is demonstrated as a promising resistive switching layer for flexible resistive random access memory (RRAM) devices. For this study, WS 2 nanoparticle solution was prepared by liquid exfoliation process from WS 2 powder and comprehensive material investigation was performed to understand the suitability for device fabrication through morphologies and electronic behavior. Devices were fabricated on indium tin oxide (ITO) coated flexible polyethylene terephthalate (PET) with ITO acting as bottom electrode (BE) and silver (Ag) deposited as top electrode (TE) with thin film of WS 2 prepared by spin coating as an active layer between electrodes. These fabricated flexible RRAM devices exhibited resistive switching characteristics with low operating voltages ( V SET ∼0.5 V and V RESET ∼−1.4 V) over 100 consecutive cycles, along with impressive retention time of ∼10 4 s and high I ON / I OFF of ∼10 4 . The performance variation of these devices was also investigated upon bending at radii of 12 mm and 5 mm indicating consistent switching, however a decay in LRS was observed after 250 s upon investigation of retention. These findings suggest that solution-processed thin films of WS 2 nanomaterial can act as a promising switching layer for flexible electronics.
Source: Nano Express
Authors: Shalu Saini, Shree Prakash Tiwari
Institution: Indian Institute of Technology Jodhpur
Language: English
Subfield: Electrical and Electronic Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,085
OpenAlex ID: W4404801492