Ultra-low cycle fatigue of ship hull structure – an alternately-cyclically loaded four-point bending test of a large box girder

Year: 2024

Type: article

Abstract: • An alternately-cyclically loaded four-point bending test of a large box girder is introduced to represent the ultra-low cycle fatigue (ULCF) of ship hull structure. During the test, large deformation is applied to the specimen even after reaching its ultimate hull girder strength (UHGS), thus extensive plastic deformation and obvious fracture can occur on the box girder. • The severely damaged specimen is further tested until 1.5 cycles of bending are finished, thus the test of post-damage box girder is realized. • The box girder is divided into 3 sub-sections, which show different but still interacting structural behavior. • The structural resistance against bending, as well as the load applied, is higher than that in the existing research works regarding ULCF of ship structures. Ultra-low cycle fatigue (ULCF) refers to material failure at small number of loading cycles. For large complex structures like ships, the damage from ULCF can bring hazardous consequences. In this study, an alternately-cyclically loaded four-point bending test of a large box girder is introduced as the specimen to represent the ULCF of ship hull structure. In every load during the test, large deformation is applied to the specimen even after reaching its ultimate hull girder strength (UHGS), thus extensive plastic deformation and obvious fracture can occur in the specimen. The severely damaged specimen is further tested until 1.5 cycles of bending are finished, thus the test of post-damage box girder is realized. Moreover, the box girder is divided into 3 sub-sections, which show different but still interacting structural behavior. The result of the test shows the structural behavior of a large complex structure suffering severe damage during alternate hogging and sagging after reaching its UHGS, which corresponds to the consequence of ULCF. The presented ULCF test also provides experiences for investigations of large complex structures with existing damages or after accidental loads. Considering the number of cycles in the test, this study can bridge the gap between monotonic overload and ultra-low cycle fatigue.

Source: Marine Structures

DOI: 10.1016/j.marstruc.2024.103732

Authors: Shi Song, Sören Ehlers, Franz von Bock und Polach, Moritz Braun

Institutions: Hamburg University of Technology, Deutsches Zentrum für Luft- und Raumfahrt e. V. (DLR)

Language: English

Topic: Fatigue and fracture mechanics

Subfield: Mechanics of Materials

Field: Engineering

Domain: Physical Sciences

SDG: Industry, innovation and infrastructure

Open Access status: hybrid

Estimated APC paid: $4,130