The effect of photoinitiator systems on resin-based composite containing ZnO-nanoparticles
Year: 2024
Type: article
Abstract: OBJECTIVE: Zinc oxide (ZnO) powder possesses antibacterial activity and although white in color, it can severely reduce the depth of cure (DoC) of resin-based composite (RBC). This study investigated the effect of unary and binary photoinitiator systems on the DoC and degree of conversion (DC) of formulated RBC containing ZnO-nanoparticles. METHODS: Fourteen RBCs (n = 3/group) were formulated consisting of 50 wt% mixture of monomers (Bis-GMA, TEGDMA, and UDMA) and 50 wt% fillers (inert barium glass powder and silica nanoparticles). ZnO-nanoparticles were added at 0 (control), 0.5, 1, 1.5 and 2 wt%. A unary initiator system consists of camphorquinone (CQ) 0.25, 0.5 and 1 wt% and ethyl 4-(dimethylamino)benzoate (EDMAB) 0.75 wt% or a binary initiator system consisting of diphenyliodonium hexafluorophosphate (DPI) 0.25, 0.5 and 1 wt%, CQ 0.25, 0.5 and 1 wt% and EDMAB 0.75 wt% were added to the monomer mixture. To measure the DoC, each specimen was prepared in a custom-made mold with a slot (16 x 8×2 mm) and a top cover plate, irradiated from one end (40 s), stored dry (37° C, 1 d) and measured at increasing depths using Vickers hardness (0.5 mm intervals). 1 mm thick specimens were prepared to measure DC continuously using FTIR, from zero up to 24 h post-irradiation. RESULTS: of binary groups ranged from 8.1 % to 10.1 %/s, and unary groups ranged from 5.2 % to 7.2 %/s. SIGNIFICANCE: The addition of DPI resulted in an overall increased curing depth, which was enhanced when lower concentrations of photoinitiators were used. Also, DPI resulted in faster conversions. This is desirable in designing antibacterial RBC containing ZnO.
Source: Dental Materials
Institutions: King Saud University, University of Manchester
Language: English
Subfield: Orthodontics
Field: Dentistry
Domain: Health Sciences
Open Access status: hybrid
Estimated APC paid: $4,170
OpenAlex ID: W4405100092