Emergence of Near-Infrared Photoluminescence via ZnS Shell Growth on the AgBiS2 Nanocrystals
Year: 2024
Type: article
Abstract: AgBiS 2 nanocrystals (NCs), composed of nontoxic, earth-abundant materials and exhibiting an exceptionally high absorption coefficient from visible to near-infrared (>10 5 cm –1 ), hold promise for photovoltaics but have lack of photoluminescence (PL) due to intrinsic nonradiative recombination and challenging shell growth. In this study, we reported a facile wet-chemical approach for the epitaxial growth of ZnS shell on AgBiS 2 NCs, which triggered the observation of PL emission in the near-infrared (764 nm). Since high quality of the core is critical for epitaxial shell growth, we first obtained rock-salt structured AgBiS 2 NCs with high crystallinity, nearly spherical shape and monodisperse size distribution (<6%) via a dual-ligand approach reacting Ag–Bi oleate with elemental sulfur in oleylamine. Next, a zincblende ZnS shell with a low-lattice mismatch of 4.9% was grown on as-prepared AgBiS 2 NCs via a highly reactive zinc (Zn(acac) 2 ) precursor that led to a higher photoluminescence quantum yield (PLQY) of 15.3%, in comparison with a relatively low reactivity precursor (Zn(ac) 2 ) resulting in reduced PLQY. The emission from AgBiS 2 NCs with ultrastrong absorption, facilitated by shell growth, can open up new possibilities in lighting, display, and bioimaging.
Source: Chemistry of Materials
Authors: Asim Onal, Tarik Safa Kaya, Önder Metin, Sedat Nizamoglu
Institution: Koç University
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $4,500
Award: Retinal Mesh Optoelectronics
OpenAlex ID: W4405274277