Strain rate-dependent failure modes of material extrusion-based additively manufactured PETG: A study on crack deflection and penetration
Year: 2024
Type: article
Abstract: • Printing orientation can influence the failure mode. • Failure modes are strain rate-dependent. • Evaluation of a strength-based approach for failure mode prediction. • Matrix/interface strength ratio plausible for moderate to high strain rates. • Accurate failure mode prediction is not possible for low strain rates. The layer-by-layer nature of fused filament fabrication (FFF) introduces interfaces along the build direction (z-axis). A crack approaching an interface may deflect or penetrate subsequent layers, based on the relative strengths of the interface and the matrix. This study evaluates the applicability of the Cook & Gordan (C&G) model for predicting crack deflection or penetration in glycol-modified poly(ethylene terephthalate) (PETG) printed structures, considering different print orientations and layer heights. The loading rate was varied between 0.1 and 1000 mm/min to identify potential rate-dependent effects. Interface and matrix strengths were determined through tensile testing, and their ratio was used to assess the validity of the C&G criterion. The results, supported by fracture mechanical validation experiments, indicate that the C&G model can effectively predict crack paths in FFF-printed PETG structures, provided that the assumptions of linear elastic fracture mechanics are not significantly violated. Accurate predictions were unattainable at the lowest loading rate (0.1 mm/min). For loading rates ≥ 10 mm/min the criterion appears plausible, aligning with previous studies.
Institution: Montanuniversität Leoben
Language: English
Subfield: Automotive Engineering
Field: Engineering
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,620
OpenAlex ID: W4405516268