Anti-corrosion and cytotoxicity properties of inorganic surface treatments on Mg1Ca biodegradable alloy
Year: 2024
Type: article
Abstract: In this work biodegradable Mg1Ca alloy underwent surface modification using hydroxyapatite (HAp), aluminium oxide (Al 2 O 3 ), and treatments with phosphoric (H 3 PO 4 ), hydrofluoric (HF), and acetic (CH 3 COOH) acids. The resulting surface-treated Mg substrates were assessed in terms of phase content and chemical composition through X-ray diffraction (XRD) and glow discharge optical emission spectrometry (GDOES). Additionally, atomic force microscopy (AFM) and scanning electron microscopy (SEM) were employed to examine the surface's topography and structure, while the corrosion behavior and cytotoxicity were surveyed using electrochemical impedance spectroscopy (EIS), alongside WST-1 reduction and lactate dehydrogenase (LDH) release assays on L929 mouse fibroblasts. The findings indicated that the surfaces of all samples were uniformly structured, while chemical analysis of the treated surfaces suggested the presence of mostly thin films. Furthermore, EIS results highlighted that the HAp-treated Mg1Ca alloy exhibited superior corrosion resistance, and the cytotoxicity assessment of Mg1Ca-HAp and Mg1Ca-H 3 PO 4 alloys showed minimal cytotoxic effects on mouse fibroblasts, compared to other treated surfaces, suggesting enhanced biocompatibility of those two surface treatments. Overall, this constitutes the first comparative study of different surface treatments developed on biodegradable Mg1Ca alloy, aiming to identify optimal modification strategies for biomedical applications. • Different surface treatments were applied to biodegradable Mg1Ca. • Most treatments resulted in thin, amorphous films, which altered chemical composition and, in some cases, topography. • The best corrosion protection was achieved with hydroxyapatite conversion film. • Phosphoric acid and hydroxyapatite-based treatments showed the lowest cytotoxicity among the studied treatments.
Source: Surface and Coatings Technology
Language: English
Subfield: Biomaterials
Field: Materials Science
Domain: Physical Sciences
Open Access status: hybrid
Estimated APC paid: $3,770
Awards: CICECO-Instituto de Materiais de Aveiro, G1516346500, G1763632427, G1792064735, G1857155500, G1918496035, G2342356290, G243576772, Unidade de Investigação em Epidemiologia - Instituto de Saúde Pública da Universidade do Porto, G274581676, G2878203709, G29311093, G3283876815, G3592153812, G3615221479, G3840324753, G4046065984, G404710190, G4448273050, Laboratório para a Investigação Integrativa e translacional em Saúde Populacional, G5224927334, CICECO – Instituto de Materiais de Aveiro, G5609873722, G5820046185, G6193589897, CICECO-Instituto de Materiais de Aveiro, G6410266313, G6997658380, G7403097962, G7965899483, G8050181529, G8108719017, G841320811
OpenAlex ID: W4405820823