Preparation and Characterization of SrFe12O19/rGO and SrFe12O19/SiO2 based Composite Materials for Enhancement of Microwave Absorption Properties
Year: 2024
Type: article
Abstract: In this work, we synthesized and investigated the microwave absorption properties of SrFe12O19, SrFe12O19/rGO and SrFe12O19/SiO2 materials prepared by chemical method. The phase structure, surface morphology, magnetic properties, and electromagnetic wave absorption characteristics of the samples were studied and compared. The SEM images of SrFe12O19/rGO sample showed a good stability in the distribution and dispersion of SrFe12O19 nanoparticles on rGO sheets. For SrFe12O19/SiO2 composite samples, it is shown that SiO2 coating is enwrapped on the SrFe12O19 surface, forming SrFe12O19/SiO2 nanocomposites with core-shell structure. The average particle size was found in the range of 60 – 120 nm. The composite SrFe12O19/rGO sample exhibited a minimum reflection loss reached -56.21 dB at 18 GHz with EAB of 12 GHz with a thickness of 3.5 mm. One can suggest that composite SrFe12O19/rGO materials possessing a best performance in both reflectivity and bandwidth can be used in the field of microwave absorption.
Institution: Hanoi University of Science and Technology
Language: English
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
Funder: Trường Đại học Bách Khoa Hà Nội
OpenAlex ID: W4405830465