Heterostructured Al2O3 @ BNNS / epoxy ‐ POSS /epoxy composites with excellent thermal conductivity, dielectric, and thermal properties

Year: 2024
Type: article
Abstract: High thermal conductivity (λ) composite with excellent dielectric, mechanical, and thermal properties are critical to the reliability and safety of electrical devices. However, the excessive addition of thermal conductive fillers may lead to severe performance degradation. Heterogeneous structured alumina‐hexagonal boron nitride nanosheets (Al2O3@BNNS) fillers were prepared by electrostatic self‐assembly method. Owing to synergistic effect of spherical Al2O3 and sheet BN, and much low interface thermal resistance, λ of the epoxy resin with 20 wt% Al2O3@BNNS2 is raised to 0.84 W·m−1·K−1, 86.67% higher than that of Al2O3/BN/EP composite. Furthermore, epoxy‐based polyhedral oligomeric silsesquioxane (EP‐POSS) was incorporated to further optimize dielectric property of the composite. The λ of the composite is slightly decreased, but the dielectric constant and dielectric loss are reduced to 2.954 and 0.01058, respectively, due to the unique cage structure of EP‐POSS and excellent compatibility of EP‐POSS with the matrix. The composite also exhibits favorable mechanical properties with an impact strength of 86.2 MPa and a bending strength of 7.81 kJ·m−2, as well as outstanding thermal stability, suggesting its promising prospects for advanced electronic devices. Highlights fAl2O3 and fBNNS electrostatic self‐assemble into heterostructured fillers. The λ of Al2O3@BNNS2/EP composite is much higher than the others. The cage‐like EP‐POSS is used to improve dielectric properties of the epoxy resin. The ε and tanδ of composites at 1 MHz are only 2.954 and 0.01058, respectively.
DOI: 10.1002/pc.29431
Language: English
Open Access status: bronze
Award: G387539346
OpenAlex ID: W4405886354
FWCI: 0.76
Cites: 44
Cited by: 8
Related to: 10