Abstract: Alloys based on titanium nick elide are widely used in medicine as implants. Nichrome wire has gained particular popularity, it is used to manufacture mesh implants used in working elements for orthodontic devices, artificial ligaments for tendon ruptures, etc. However, before manufacturing products from titanium nick elide wire, the latter is subjected to heat treatment to give the desired shape during the compression process. Many works are devoted to the study of annealing of wires more than 1 mm thick, so the purpose of this work will be to present the results of studying the structure and mechanical properties of titanium nick elide wires with a diameter of 100 μm, annealed at 300, 400, 500, 600 °C. The deformation behavior of the wire was studied after tensile strength tests. The obtained tensile curves describe its mechanical properties and super elasticity. The fracture surface of the wire was examined on a scanning electron microscope with an energy-dispersive X-ray analyzer. Fractographic analysis of the main fracture characteristics was also performed. It was found that the tensile strength and martensitic shear stress decrease with increasing annealing temperature. The annealing conditions determined by the obtained results do not suppress the super elasticity of the wire, but impart strength and ductility necessary for medical purposes. Wire samples annealed at 300 and 400 °C demonstrate similar super elastic behavior in cyclic tests characterized by mechanical hysteresis and 1 % residual deformation. Annealing of 100 μm thick wire at 500 and 600 °C provoked greater residual deformation after cyclic tests.
Source: Russian journal of biomechanics
Language: English
Subfield: Materials Chemistry
Field: Materials Science
Domain: Physical Sciences
Open Access status: diamond
Funder: Russian Science Foundation
OpenAlex ID: W4406628517