Structural, surface, electrical and UVC sensing properties of high temperature RF sputtered gallium oxide thin films
Year: 2025
Type: article
Abstract: Gallium oxide thin films have been deposited on a-, c-, r- plane sapphire and amorphous Si 3 N 4 at 800 °C by RF sputtering from a 99.99 % purity Ga 2 O 3 target then characterised structurally, optically and electrically. A fixed process pressure of 3.0 mTorr was employed with O 2 :Ar ratios of 0:1 (0 % O 2 ), 1:18 (5 % O 2 ), 1:9 (10 % O 2 ) and 3:17 (15 % O 2 ). X-ray diffractograms attributable to β-Ga 2 O 3 were collected from the films grown on a- and c- plane sapphire. The highest crystallinity was observed in the films grown on c-plane sapphire. Ga 2 O 3 films on r-plane sapphire and Si 3 N 4 produced no diffracted peaks and were deemed to be amorphous or nanocrystalline. Ga 3d X-ray photoelectron spectra showed only Ga-O bonding with no evidence of Ga-Ga bonding, even in the films deposited with only Ar introduced to the chamber. Direct optical bandgaps exceeding 5.0 eV were observed in the films on a- and c- plane sapphire. Valence band spectra showed the valence band maxima (VBM) and Fermi level (FL) were separated by ∼3 eV in the Ga 2 O 3 films on a- and c- plane sapphire whilst films on r-plane sapphire exhibited VBM - FL gaps of ∼2.5 eV, indicative of low shallow impurity/defect doping density, most likely due to oxygen vacancies. Selected films were incorporated into metal-semiconductor-metal UV-C detectors. Solar-blind detection was confirmed and the maximum measured UV-C /dark current ratios (I UVC :I dark ) exceeded 10 3 :1.
Source: Materials Today Electronics
Authors: Sidhant Sharma, Hilal Nagib, Phuong Y. Le, Martin W. Allen, Anthony S. Holland, Jim G. Partridge, Hiep N. Tran
Language: English
Topic: Ga2O3 and related materials
Field: Materials Science
Domain: Physical Sciences
Open Access status: gold
Estimated APC paid: $2,860
OpenAlex ID: W4407086702